SABIC沙伯基礎創新塑料PBT Valox 325M物性參數物性表
以下是SABIC沙伯基礎創新塑料PBT Valox 325M的中英文物性表
|
SABIC Innovative Plastics Valox? 325M PBT (Asia Pacific)
The property table is provided by www.plas-cn.com, welcome to download, reprint please indicate the source!
|
|||
|
Physical Properties物理性質
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Specific Gravity比重
|
1.31 g/cc
|
1.31 g/cc
|
ASTM D 792
|
|
Water Absorption吸水率
|
0.10 %
@Time 86400 sec |
0.10 %
@Time 24.0 hour |
ASTM D 570
|
|
Moisture Absorption at Equilibrium吸濕平衡
|
0.34 %
@Temperature 23.0 °C |
0.34 %
@Temperature 73.4 °F |
ASTM D 570
|
|
Linear Mold Shrinkage, Flow線性收縮率/流動
|
0.0090 - 0.016 cm/cm
@Thickness 0.750 - 2.30 mm |
0.0090 - 0.016 in/in
@Thickness 0.0295 - 0.0906 in |
SABIC Method
|
|
0.015 - 0.023 cm/cm
@Thickness 2.30 - 4.60 mm |
0.015 - 0.023 in/in
@Thickness 0.0906 - 0.181 in |
SABIC Method
|
|
|
Linear Mold Shrinkage, Transverse線性收縮率/橫向
|
0.010 - 0.017 cm/cm
@Thickness 0.750 - 2.30 mm |
0.010 - 0.017 in/in
@Thickness 0.0295 - 0.0906 in |
SABIC Method
|
|
0.016 - 0.024 cm/cm
@Thickness 2.30 - 4.60 mm |
0.016 - 0.024 in/in
@Thickness 0.0906 - 0.181 in |
SABIC Method
|
|
|
Mechanical Properties力學性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Hardness, Rockwell R羅氏硬度R
|
119
|
119
|
ASTM D 785
|
|
Tensile Strength, Yield屈服拉伸強度
|
48.0 MPa
|
6960 psi
|
Type I, 50 mm/min; ASTM D 638
|
|
Elongation at Break斷裂伸長率
|
180 %
|
180 %
|
Type I, 50 mm/min; ASTM D 638
|
|
Flexural Yield Strength彎曲屈服強度
|
81.0 MPa
|
11700 psi
|
1.3 mm/min, 50 mm span; ASTM D 790
|
|
Flexural Modulus彎曲彈性模量
|
2.34 GPa
|
339 ksi
|
1.3 mm/min, 50 mm span; ASTM D 790
|
|
Izod Impact, Notched懸臂梁缺口沖擊強度
|
0.530 J/cm
@Temperature 23.0 °C |
0.993 ft-lb/in
@Temperature 73.4 °F |
ASTM D 256
|
|
Izod Impact, Unnotched懸臂梁無缺口沖擊強度
|
16.02 J/cm
@Temperature 23.0 °C |
30.01 ft-lb/in
@Temperature 73.4 °F |
ASTM D 4812
|
|
Gardner Impact加德納的影響
|
40.0 J
@Temperature 23.0 °C |
29.5 ft-lb
@Temperature 73.4 °F |
ASTM D 3029
|
|
Electrical Properties電性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Volume ResiSTivity體積電阻率
|
>= 2.20e+16 ohm-cm
|
>= 2.20e+16 ohm-cm
|
ASTM D 257
|
|
Dielectric Constant介電常數
|
3.13
@Frequency 1.00e+6 Hz |
3.13
@Frequency 1.00e+6 Hz |
ASTM D 150
|
|
3.17
@Frequency 100 Hz |
3.17
@Frequency 100 Hz |
ASTM D 150
|
|
|
Dielectric Strength介電強度
|
17.8 kV/mm
@Thickness 3.20 mm |
452 kV/in
@Thickness 0.126 in |
in air; ASTM D 149
|
|
Dissipation Factor耗散因數
|
0.0014
@Frequency 100 Hz |
0.0014
@Frequency 100 Hz |
ASTM D 150
|
|
0.0098
@Frequency 1.00e+6 Hz |
0.0098
@Frequency 1.00e+6 Hz |
ASTM D 150
|
|
|
Arc Resistance 耐電弧性
|
180 - 240 sec
|
180 - 240 sec
|
Tungsten, PLC code 4; ASTM D 495
|
|
Comparative Tracking Index相對漏電起痕指數
|
>= 600 V
|
>= 600 V
|
PLC code 0; UL 746A
|
|
Hot Wire Ignition, HWI熱線圈點燃測試
|
15 - 30 sec
|
15 - 30 sec
|
PLC code 3; UL 746A
|
|
High Amp Arc Ignition, HAI高電流電弧點燃測試
|
>= 120 arcs
|
>= 120 arcs
|
surface, PLC code 0; UL 746A
|
|
High Voltage Arc-Tracking Rate, HVTR高壓電弧跟蹤速度
|
10.0 - 25.4 mm/min
|
0.394 - 1.00 in/min
|
PLC code 1; UL 746A
|
|
Thermal Properties熱性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Deflection Temperature at熱變形溫度0.46 MPa (66 psi)
|
150 °C
@Thickness 6.40 mm |
302 °F
@Thickness 0.252 in |
unannealed; ASTM D 648
|
|
Deflection Temperature at熱變形溫度1.8 MPa (264 psi)
|
55.0 °C
@Thickness 6.40 mm |
131 °F
@Thickness 0.252 in |
unannealed; ASTM D 648
|
|
UL RTI, Electrical相對溫度指數
|
120 °C
|
248 °F
|
UL 746B
|
|
UL RTI, Mechanical with Impact機械沖擊熱指數
|
120 °C
|
248 °F
|
UL 746B
|
|
UL RTI, Mechanical without Impact無機械沖擊熱指數
|
140 °C
|
284 °F
|
UL 746B
|
|
Flammability, UL94阻燃等級
|
HB
@Thickness 0.830 mm |
HB
@Thickness 0.0327 in |
UL 94
|