點擊圖片查看大圖耐沖ABS CYCOLAC EX39 沙伯基礎 耐低溫ABS 擠出級ABS
Highest impact extrusion ABS for sheet and blow molding applications.
EX39 物性表：
| REVISION: 03/07/2019 Compare this region | ||||
|---|---|---|---|---|
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 35 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 28 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3.5 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 108 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 1680 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 57 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1900 | MPa | ASTM D 790 | |
| IMPACT | ||||
| Izod Impact, notched, 23°C | 464 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 320 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 39 | J | ASTM D 3763 | |
| THERMAL | ||||
| Vicat Softening Temp, Rate B/50 | 106 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 91 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 77 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 1.01E-04 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 1.17E-04 | 1/°C | ASTM E 831 | |
| Relative Temp Index, Elec | 60 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 60 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 60 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.03 | - | ASTM D 792 | |
| Mold Shrinkage, flow, 3.2 mm | 0.7-0.9 | % | SABIC method | |
| Melt Viscosity, 240°C, 100 sec-1 | 15200 | Poise | ASTM D 3825 | |
| Melt Volume Rate, MVR at 220°C/10.0 kg | 4 | cm3/10 min | ISO 1133 | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94HB Flame Class Rating | 1.52 | mm | UL 94 | |
| EXTRUSION BLOW MOLDING | ||||
| Drying Temperature | 80-90 | °C | ||
| Drying Time | 5-4 | hrs | ||
| Drying Time (Cumulative) | 24 | hrs | ||
| Maximum Moisture Content | 0.02-0.04 | % | ||
| Minimum Moisture Content | 0.04 | % | ||
| Melt Temperature (Parison) | 210-225 | °C | ||
| Barrel - Zone 1 Temperature | 190-220 | °C | ||
| Barrel - Zone 2 Temperature | 190-220 | °C | ||
| Barrel - Zone 3 Temperature | 190-220 | °C | ||
| Barrel - Zone 4 Temperature | 190-220 | °C | ||
| Adapter - Zone 5 Temperature | 195-220 | °C | ||
| Head - Zone 6 - Top Temperature | 195-220 | °C | ||
| Head - Zone 7 - Bottom Temperature | 195-220 | °C | ||
| Screw Speed | 20-60 | rpm | ||
| Extruder Feed Zone Temperature | 60-80 | °C | ||
| Mold Temperature | 40-90 | °C | ||
| Die Temperature | 195-220 | °C | ||
| SHEET EXTRUSION | ||||
| Drying Temperature | 90-95 | °C | ||
| Drying Time | 2-4 | hrs | ||
| Maximum Moisture Content | 0 | % | ||
| Melt Temperature | 210-240 | °C | ||
| Barrel - Zone 1 Temperature | 195-210 | °C | ||
| Barrel - Zone 2 Temperature | 200-220 | °C | ||
| Barrel - Zone 3 Temperature | 205-230 | °C | ||
| Barrel - Zone 4 Temperature | 210-235 | °C | ||
| Adapter Temperature | 200-225 | °C | ||
| Die Temperature | 210-240 | °C | ||