點擊圖片查看大圖抗紫外線ABS CYCOLAC MG38U NA1000
Improved UV performance, very high impact ABS. Toughness/rigidity. Good fatigue resistance.
改善紫外線性能，非常高的抗沖擊性。韌性/剛性?？蛊谛阅芎谩?/p>
MG38U物性表：
| REVISION: 24/09/2019 Compare this region | ||||
|---|---|---|---|---|
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 43 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 36 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 2.9 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 98 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 2390 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 76 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2410 | MPa | ASTM D 790 | |
| Tensile Stress, yield, 5 mm/min | 41 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 33 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 2.5 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 30 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 2410 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 70 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 2310 | MPa | ISO 178 | |
| IMPACT | ||||
| Izod Impact, notched, 23°C | 374 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 32 | J | ASTM D 3763 | |
| Izod Impact, notched 80*10*4 +23°C | 27 | kJ/m2 | ISO 180/1A | |
| THERMAL | ||||
| Vicat Softening Temp, Rate B/50 | 98 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 97 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 82 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 8.82E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 8.64E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, flow | 8.82E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 8.64E-05 | 1/°C | ISO 11359-2 | |
| Vicat Softening Temp, Rate B/50 | 98 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 99 | °C | ISO 306 | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 80 | °C | ISO 75/Af | |
| PHYSICAL | ||||
| Specific Gravity | 1.05 | - | ASTM D 792 | |
| Mold Shrinkage, flow, 3.2 mm | 0.5-0.8 | % | SABIC method | |
| Density | 1.05 | g/cm3 | ISO 1183 | |
| Water Absorption, (23°C/sat) | 1 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.2 | % | ISO 62 | |
| Melt Flow Rate, 220°C/10.0 kg | 15 | g/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 220°C/5.0 kg | 5 | cm3/10 min | ISO 1133 | |
| FLAME CHARACTERISTICS | ||||
| UL Yellow Card | E121562-100095483 | - | - | |
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 | |
| INJECTION MOLDING | ||||
| Drying Temperature | 80-95 | °C | ||
| Drying Time | 2-4 | hrs | ||
| Drying Time (Cumulative) | 8 | hrs | ||
| Maximum Moisture Content | 0.1 | % | ||
| Melt Temperature | 220-260 | °C | ||
| Nozzle Temperature | 220-260 | °C | ||
| Front - Zone 3 Temperature | 215-240 | °C | ||
| Middle - Zone 2 Temperature | 205-225 | °C | ||
| Rear - Zone 1 Temperature | 190-210 | °C | ||
| Mold Temperature | 50-70 | °C | ||
| Back Pressure | 0.3-0.7 | MPa | ||
| Screw Speed | 30-60 | rpm | ||
| Shot to Cylinder Size | 50-70 | % | ||
| Vent Depth | 0.038-0.051 | mm | ||