TYPICAL PROPERTIES (1)
|
|
MECHANICAL
|
Value
|
Unit
|
Standard
|
|
Tensile Stress, yld, Type I, 50 mm/min
|
62
|
MPa
|
ASTM D 638
|
|
Tensile Stress, brk, Type I, 50 mm/min
|
65
|
MPa
|
ASTM D 638
|
|
Tensile Strain, yld, Type I, 50 mm/min
|
7
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
110
|
%
|
ASTM D 638
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
93
|
MPa
|
ASTM D 790
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
2340
|
MPa
|
ASTM D 790
|
|
Hardness, Rockwell M
|
70
|
-
|
ASTM D 785
|
|
Hardness, Rockwell R
|
118
|
-
|
ASTM D 785
|
|
Taber Abrasion, CS-17, 1 kg
|
10
|
mg/1000cy
|
ASTM D 1044
|
|
Tensile Stress, yield, 50 mm/min
|
63
|
MPa
|
ISO 527
|
|
Tensile Stress, break, 50 mm/min
|
63
|
MPa
|
ISO 527
|
|
Tensile Strain, yield, 50 mm/min
|
6
|
%
|
ISO 527
|
|
Tensile Modulus, 1 mm/min
|
2300
|
MPa
|
ISO 527
|
|
Flexural Stress, yield, 2 mm/min
|
94
|
MPa
|
ISO 178
|
|
Flexural Modulus, 2 mm/min
|
2300
|
MPa
|
ISO 178
|
|
IMPACT
|
Value
|
Unit
|
Standard
|
|
Izod Impact, unnotched, 23°C
|
3200
|
J/m
|
ASTM D 4812
|
|
Izod Impact, notched, 23°C
|
750
|
J/m
|
ASTM D 256
|
|
Tensile Impact, Type S
|
546
|
kJ/m2
|
ASTM D 1822
|
|
Falling Dart Impact (D 3029), 23°C
|
169
|
J
|
ASTM D 3029
|
|
THERMAL
|
Value
|
Unit
|
Standard
|
|
Vicat Softening Temp, Rate B/50
|
154
|
°C
|
ASTM D 1525
|
|
HDT, 0.45 MPa, 6.4 mm, unannealed
|
137
|
°C
|
ASTM D 648
|
|
HDT, 1.82 MPa, 6.4 mm, unannealed
|
132
|
°C
|
ASTM D 648
|
|
CTE, -40°C to 95°C, flow
|
6.84E-05
|
1/°C
|
ASTM E 831
|
|
Specific Heat
|
1.26
|
J/g-°C
|
ASTM C 351
|
|
Thermal Conductivity
|
0.29
|
W/m-°C
|
ASTM C 177
|
|
Ball Pressure Test, 125°C +/- 2°C
|
PASSES
|
-
|
IEC 60695-10-2
|
|
Vicat Softening Temp, Rate B/120
|
145
|
°C
|
ISO 306
|
|
Relative Temp Index, Elec
|
80
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact
|
80
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/o impact
|
80
|
°C
|
UL 746B
|
|
PHYSICAL
|
Value
|
Unit
|
Standard
|
|
Specific Gravity
|
1.2
|
-
|
ASTM D 792
|
|
Specific Volume
|
0.83
|
cm3/g
|
ASTM D 792
|
|
Density
|
1.19
|
g/cm3
|
ASTM D 792
|
|
Water Absorption, 24 hours
|
0.15
|
%
|
ASTM D 570
|
|
Water Absorption, equilibrium, 23C
|
0.35
|
%
|
ASTM D 570
|
|
Water Absorption, equilibrium, 100°C
|
0.58
|
%
|
ASTM D 570
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.5 - 0.7
|
%
|
SABIC Method
|
|
Melt Flow Rate, 300°C/1.2 kgf
|
7
|
g/10 min
|
ASTM D 1238
|
|
Melt Volume Rate, MVR at 300°C/1.2 kg
|
7
|
cm3/10 min
|
ISO 1133
|
|
OPTICAL
|
Value
|
Unit
|
Standard
|
|
Refractive Index
|
1.586
|
-
|
ASTM D 542
|
|
ELECTRICAL
|
Value
|
Unit
|
Standard
|
|
Volume Resistivity
|
>1.E+17
|
Ohm-cm
|
ASTM D 257
|
|
Dielectric Strength, in air, 3.2 mm
|
15
|
kV/mm
|
ASTM D 149
|
|
Relative Permittivity, 50/60 Hz
|
3.17
|
-
|
ASTM D 150
|
|
Relative Permittivity, 1 MHz
|
2.96
|
-
|
ASTM D 150
|
|
Dissipation Factor, 50/60 Hz
|
0.0009
|
-
|
ASTM D 150
|
|
Dissipation Factor, 1 MHz
|
0.01
|
-
|
ASTM D 150
|
|
Hot Wire Ignition {PLC)
|
3
|
PLC Code
|
UL 746A
|
|
High Ampere Arc Ign, surface {PLC}
|
1
|
PLC Code
|
UL 746A
|
|
Comparative Tracking Index (UL) {PLC}
|
3
|
PLC Code
|
UL 746A
|
|
FLAME CHARACTERISTICS
|
Value
|
Unit
|
Standard
|
|
UL Recognized, 94V-2 Flame Class Rating (3)
|
0.75 - 1.65
|
mm
|
UL 94
|
|
Glow Wire Flammability Index 750°C, passes at
|
0.75
|
mm
|
IEC 60695-2-12
|
|
Glow Wire Flammability Index 850°C, passes at
|
1.5
|
mm
|
IEC 60695-2-12
|
|
Glow Wire Ignitability Temperature, 0.75 mm, by VDE
|
875
|
°C
|
IEC 60695-2-13
|
|
Glow Wire Ignitability Temperature, 1.5 mm
|
850
|
°C
|
IEC 60695-2-13
|
|
UV-light, water exposure/immersion
|
F2
|
-
|
UL 746C
|